Kontakti

Na voljo smo vam od ponedeljka do petka med 8:00 in 17:00 uro. Na tej povezavi najdete kontaktne osebe za svojo regijo.

Centrala Wolfurt
+43 5574 6706-0

Vaša kontaktna oseba

Trgovina

Košarica {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} izdelek Zamenjaj košarico

Opomba

Slika

izdelek

Kos

Cene po pozicijah

Skupna cena

Skupna cena s popustom

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Prosimo vas, da se prijavite, da bi lahko videli vaše cene ter nadaljevali z naročilom.

Naš izbran nabor omogoča za skoraj vsak primer uporabe ustrezen material.

1.2083 / 1.2083 ESU Steel for through hardening

Designation

DIN:	X 40 Cr 14
AFNOR:	Z 40 C 14
UNI:	-
AISI:	420 / 420 ESR

Chemical composition:

C	0.40
Si	0.40
Mn	0.30
Cr	13.00

Strength:

max. 240 HB
(≈ max. 800 N/mm²)

Thermal conductivity at 100 °C:

18 W/m K

Character:

low corrosion, high-alloy, low warpage steel for through hardening with excellent properties for mirror polishing as well as good photoetching, good machinability, high wear resistance and high dimensional stability

Application:

mould plates and inserts for working with chemically aggressive plastics; because of excellent polishing, suitable for optical and medical products

Treatment by

Polishing:
can be polished in the annealed and hardened state; good preliminary surface preparation work is decisive for a good polish

Etching:
good photoetching (graining)

EDM:
in the hardened and tempered condition, treat again for stress relief about 20°C below the last temperature
unusual:

Nitriding, hard chroming

Heat treatment:

Soft annealing:
750 to 800°C for about 2 to 5 hours
slow controlled cooling of 10 to 20°C per hour to about 650°C; further cooling in air, max. 200 HB

Hardening:
1000°C to 1050°C
15 to 30 minutes keeping curing temperature
quenching in oil/compressed gas/hot bath
obtainable hardness: 53 - 56 HRC

Tempering:
slow heating to tempering temperature immediately after hardening;
minimum time in furnace: 2 hours per 20 mm part thickness;
Tempering twice is recommended.

Annealing graph:

Technical tip

Cold-work steel
must be tempered several times after hardening (max. 52HRC). The demand for “max. hardness” often ends up in material breakage.
mould temperature max. 200°C
corrosion-resistant after hardening
The ESR quality guarantees an extremely pure and homogeneous microstructure.

To the mould making overview To the die making overview