Kontakti

Na voljo smo vam od ponedeljka do petka med 8:00 in 17:00 uro. Na tej povezavi najdete kontaktne osebe za svojo regijo.

Centrala Wolfurt
+43 5574 6706-0

Vaša kontaktna oseba

Košarica {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} izdelek   Zamenjaj košarico

Opomba

Slika izdelek Kos Cene po pozicijah Skupna cena Skupna cena s popustom
{{warenkorbItem.produktgruppe.produktname}}

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

     
{{hannexItem.Benennung}}

{{hannexItem.Bezeichnung}}

     

Prosimo vas, da se prijavite, da bi lahko videli vaše cene ter nadaljevali z naročilom.

Zmanjševanje napetosti

Naš izbran nabor omogoča za skoraj vsak primer uporabe ustrezen material.

1.2311 Tool steel

Designation

DIN:40 CrMnMo 7
AFNOR:40 CMD 8
UNI:35 CrMo 8 KU
AISI:P20

Chemical composition:

C0.40
Si0.40
Mn1.50
Cr1.90
Mo0.20

Strength:

280 - 325 HB
(≈ 950 - 1100 N/mm²)

Thermal conductivity at 100 °C:

35 W/m K


Character:

alloyed and pre-toughened tool steel, especially suitable for polishing and nitriding; high dimensional stability

Application:

cavity plates, inserts and high-tensile machine parts


Treatment by

possible:
Etching, EDM

Polishing:
excellent polishing; for higher surface requirements we recommend steel for through hardening

Nitriding:
increases the steel's wear resistance

Hard chroming:
particularly increases the steel's wear resistance and corrosion resistance


Heat treatment:

already pre-toughened; usually no heat treatment required

Nitriding:
Before nitriding, stress-relief annealing is recommended at 580 °C. (Meusburger standard)

Hard chroming:
After the hard chroming the mould must be annealed about 3 to 4 hours at 180 °C to avoid brittle fractures from hydrogen.

Hardening:
840 to 860 °C

Cooling:
to 180 °C/220 °C in oil/hot bath, then in air to about 100 °C obtainable hardness: 52 HRC

Tempering:
Slow heating to tempering temperature immediately after hardening. Minimum time in furnace: 1 hour per 25 mm part thickness

Annealing graph:


Technical tip:

  • Core strength decreases with increasing plate thickness ⇒ for thickness >300, 1.2738 is recommended.

To the mould making overview To the die making overview

Available in the web shop as:
Data sheet 1.2311

Odpri PDF

Material grades brochure

Material grades brochure

Material grades poster

Material grades poster

Prijava

Ste že registriran uporabnik?

V kolikor že imate dostop za prijavo v Meusburger portal se prosimo prijavite tukaj:

Ste pozabili geslo?

Novo generirano geslo je že na poti in bo kmalu v vašem poštnem predalu. Želimo Vam uspešen dan.

Prosimo vnesite vaš E-mail naslov.
Poslali vam bomo novo geslo.

Izberite vašo državo

Lokacije

Try our new version of 'My account'

Get familiar with our new ‘My account’ section and benefit from numerous advantages.

Now the new ‘My account’ also gives you a direct insight into the next level of the Meusburger portal. Check out all the information and benefits of the portal here.

Get familiar with our new ‘My account’ section and benefit from numerous advantages.

Now the new ‘My account’ also gives you a direct insight into the next level of the Meusburger portal. Check out all the information and benefits of the portal here.

Keep selection
Beta
New version
Current version