Contact

Vă stăm la dispoziție personal cu cea mai mare plăcere de luni până vineri între orele 8:00 și 17:00. Pe acest link ve-ți regăsi persoana de contact din regiunea dumneavoastră.

Persoana dvs. de contact

Centrala Wolfurt
+43 5574 6706-0

Service și suport

Sisteme calde
+49 6204 6069-0

Termoregulatoare
+49 6293 9203-0

Mesajul dumneavoastră către noi

Coş de cumpărături {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Articol   Schimbare coș cumpărături

Observație

Poză Articol Buc Preț unitar Preț total Preț total incl. reducere
{{warenkorbItem.produktgruppe.produktname}}

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

     
{{hannexItem.Benennung}}

{{hannexItem.Bezeichnung}}

     

Vă rugăm să vă logați pentru a vedea prețurile și pentru a continua comanda.

Reducerea tensiunii

Sortimentul nostru bine selectat are materialul potrivit pentru aproape fiecare aplicație.

1.2379 Steel for through hardening

Designation

DIN:X 153 CrMoV 12
AFNOR:Z 160 CDV 12
UNI:-
AISI:≈ D2

Chemical composition:

C1.53
Si0.30
Mn0.35
Cr12.00
Mo0.80
V
0.80

Strength:

max. 255 HB
(≈ max. 860 N/mm²)

Thermal conductivity at 100 °C:

21 W/m K


Character:

high-alloy steel for through-hardening with moderate machinability; extremely wear resistant and low warpage, good dimensional stability, toughness and through hardenability

Application:

mould plates and inserts as well as wear plates and cutting dies with increased wear resistance


Treatment by

Polishing:
possible when hardened

Nitriding:
very well suited, due to the fact that the hardness of the base material will not fall below 60 HRC

EDM:
possible, Structure eroding not possible

Hard chroming:
possible

Etching:
not possible, coarse carbides are washed out


Heat treatment:

Soft annealing:
800 to 850 °C for about 2 to 5 hours; slow controlled cooling of 10 to 20 °C per hour to about 600 °C; further cooling in air, max. 235 HB

Hardening:

1020 °C
1060 to 1080 °C
quenching in oil/air/hot bath
obtainable hardness: 63−65 HRC

Tempering:
slow heating to tempering temperature (to avoid forming of cracks) immediately after hardening; triple tempering at max. secondary hardening temperature is recommended; rapid cooling following the tempering improves the dimensional stability; maximum hardness achievable after tempering: 60-62 HRC

Annealing graph:


Technical tip:
  • secondary hardening, very good base material for nitriding or coating

To the mould making overview To the die making overview

Available in the web shop as:
Data sheet 1.2379

Deschide PDF

Material grades brochure

Material grades brochure

Material grades poster

Material grades poster

Log in

Sunteți deja client?

Dacă aveți deja date de acces pentru Portalul Meusburger, vă rugăm să vă logați aici:

Ați uitat parola?

Parola nouă este deja pe drum și trebuie să apară în scurt timp în căsuța dvs. de email. Vă dorim o zi de succes.

Vă rugăm să introduceți adresa dvs. de e-mail.
Vă vom trimite o parolă nouă.

Selecţie shop

Alegeți țara

Locații