Contact

Vă stăm la dispoziție personal cu cea mai mare plăcere de luni până vineri între orele 8:00 și 17:00. Pe acest link ve-ți regăsi persoana de contact din regiunea dumneavoastră.

Centrala Wolfurt
+43 5574 6706-0

Persoana dvs. de contact

SHOP

Coş de cumpărături {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Articol Schimbare coș cumpărături

Observație

Poză

Articol

Buc

Preț unitar

Preț total

Preț total incl. reducere

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Vă rugăm să vă logați pentru a vedea prețurile și pentru a continua comanda.

Sortimentul nostru bine selectat are materialul potrivit pentru aproape fiecare aplicație.

1.2363 Steel for through hardening

Designation

DIN:	X 100 CrMoV 5
AFNOR:	Z 100 CDV 5
UNI:	X 100 CrMoV 5-1 KU
AISI:	A2

Chemical composition:

C	1.00
Si	0.30
Mn	0.50
Cr	5.20
Mo	1.10
V	0.20

Strength:

max. 240 HB
(≈ max. 820 N/mm²)

Thermal conductivity at 100 °C:

19 W/m K

Character:

steel for through hardening with good machinability, high wear resistance and low warpage; very good dimensional stability, toughness and through hardenability

Application:

mould plates and inserts as well as cutting punches, wear plates and cutting plates with high requirements on toughness

Treatment by

is possible:
Polishing, etching, nitriding, hard chroming

Heat treatment:

Soft annealing:
800 to 840°C for about 4 to 5 hours slow controlled cooling of 10 to 20°C per hour to about 650°C further cooling in air, max. 230 HB

Hardening:
950°C to 980°C
quenching in calm air
obtainable hardness: 62 HRC

Tempering:
slow heating to tempering temperature immediately after hardening; tempering twice is recommended; rapid cooling following the tempering improves the dimensional stability;

maximum hardness achievable after tempering: 58−60 HRC

Annealing graph: