Contact

Vă stăm la dispoziție personal cu cea mai mare plăcere de luni până vineri între orele 8:00 și 17:00. Pe acest link ve-ți regăsi persoana de contact din regiunea dumneavoastră.

Centrala Wolfurt
+43 5574 6706-0

Persoana dvs. de contact

SHOP

Coş de cumpărături {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Articol Schimbare coș cumpărături

Observație

Poză

Articol

Buc

Preț unitar

Preț total

Preț total incl. reducere

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Vă rugăm să vă logați pentru a vedea prețurile și pentru a continua comanda.

Sortimentul nostru bine selectat are materialul potrivit pentru aproape fiecare aplicație.

1.2085 Tool steel

Designation

DIN:	X 33 CrS 16
AFNOR:	Z 35 CD 17.S
UNI:	-
AISI:	≈ 422 + S

Chemical composition:

C	0.33
Si	0.30
Mn	0.80
Cr	16.00
S	0.06
Ni	0.30

Strength:

280 - 325 HB
(≈ 950 - 1100 N/mm²)

Thermal conductivity at 100 °C:

18 W/m K

Character:

corrosion resistant, pre-toughened tool steel with good machinability due to Sulphur additive

Application:

plates for corrosion resistant mould bases and die sets;
moulds for corrosive plastics; the expense for protection and care of mould tools is reduced thanks to increased corrosion resistance; not suitable for mould inserts

Treatment by

unusual:
Polishing, etching, EDM, nitriding, hard chroming

Heat treatment:

Usually no heat treatment is required

Soft annealing:
850 to 880 °C for about 2 to 5 hours
slow controlled cooling, further cooling in air, annealing hardness max. 240 HB

Hardening:
1000 to 1030 °C
keeping curing temperature for 30 minutes
quenching in oil is preferable
obtainable hardness: 48 HRC

Tempering:
slow heating to tempering temperature immediately after hardening;
minimum time in furnace: 2 hour per 20 mm part thickness;
tempering twice is recommended

Annealing graph: