Contato

Estamos sempre disponíveis de segunda a sexta-feira, das 8:00 às 17:00. Utilize esta ligação para encontrar as suas pessoas de contacto consoante a sua região.

Sede em Wolfurt
+43 5574 6706-0

Os seus contactos

LOJA

Carrinho de compras {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Artigos Mudar carrinhos de compras

Observação

Imagem

Artigos

Unid.

Preço individual

Preço total

Preço total, incl. desconto

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{hannexItem.Bezeichnung}}

Por favor, inicie a sessão para ver os seus preços e para continuar com a encomenda.

Na nossa gama selecionada, pode encontrar o material adequado para praticamente qualquer aplicação.

1.3344 Powder metallurgical steel

Designation

DIN:	PM 6-5-3
AFNOR:	X 130 WMoCrV 6-5-4-3
UNI:	W 6 Mo 5 Cr 4 V 3
AISI:	M 3-2 (PM)

Chemical composition:

C	1.25
Si	0.30
Mn	0.30
Cr	4.00
Mo	5.00
V	3.00
W	6.20

Strength:

max. 265 HB
(≈ max. 905 N/mm²)

Thermal conductivity at 100 °C:

24 W/m K

Character:

powder metallurgy high-speed steel with good machinability, high resistance to adhesive and abrasive wear, with optimal toughness due to the uniform and fine carbide structure, very good through hardenability and high dimensional stability

Application:

blocks for eroding, cutting punches and dies with particularly durable edges; inserts with highest wear resistance

Treatment by

highly suitable:
Mirror polishing, nitriding, EDM, coating

Heat treatment:

Soft annealing:
860 to 880 °C for about 2 to 5 hours
slow controlled cooling of 10 to 20 °C per hour to about 600 °C; further cooling in air, max. 260 HB

Hardening:

— 1180 °C
--- 1150 °C

-·-· 1100 °C

curing temperature: see tempering chart
quenching in oil/compressed gas/air/hot bath
obtainable hardness: 64−66 HRC

Tempering:
Slow heating to tempering temperature (in order to avoid formation of cracks) immediately after hardening;
tempering three times is recommended

Annealing graph: