Contacto

Estaremos encantados de atenderle en persona de lunes a viernes desde las 8:00 hasta las 17:00 horas. Haga clic en este enlace para buscar el interlocutor que le corresponde por zona.

Sus contactos

Sede de Wolfurt
+43 5574 6706-0

Asistencia al cliente

Sistemas de cámara caliente
+49 6204 6069-0

Sistemas de regulación
+49 6293 9203-0

Su mensaje:

Carrito de la compra {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} artículos   Cambiar de carrito de la compra

Observaciones

Imagen artículos Unidades Precio por unidad Precio total Precio total con descuento
{{warenkorbItem.produktgruppe.produktname}}

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben:[{attrPrefix: 'L_', searchPattern: '/...', replacePrefix: '/', replaceSuffix: ''}] }} {{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

     
{{hannexItem.Benennung}}

{{hannexItem.Bezeichnung}}

     

Inicie sesión para ver los precios que se le aplican y continuar con el pedido.

Reducción de tensiones

Nuestra selecta gama facilita el material adecuado para cualquier aplicación.

1.2379 Steel for through hardening

Designation

DIN:X 153 CrMoV 12
AFNOR:Z 160 CDV 12
UNI:-
AISI:≈ D2

Chemical composition:

C1.53
Si0.30
Mn0.35
Cr12.00
Mo0.80
V
0.80

Strength:

max. 255 HB
(≈ max. 860 N/mm²)

Thermal conductivity at 100 °C:

21 W/m K


Character:

high-alloy steel for through-hardening with moderate machinability; extremely wear resistant and low warpage, good dimensional stability, toughness and through hardenability

Application:

mould plates and inserts as well as wear plates and cutting dies with increased wear resistance


Treatment by

Polishing:
possible when hardened

Nitriding:
very well suited, due to the fact that the hardness of the base material will not fall below 60 HRC

EDM:
possible, Structure eroding not possible

Hard chroming:
possible

Etching:
not possible, coarse carbides are washed out


Heat treatment:

Soft annealing:
800 to 850 °C for about 2 to 5 hours; slow controlled cooling of 10 to 20 °C per hour to about 600 °C; further cooling in air, max. 235 HB

Hardening:

1020 °C
1060 to 1080 °C
quenching in oil/air/hot bath
obtainable hardness: 63−65 HRC

Tempering:
slow heating to tempering temperature (to avoid forming of cracks) immediately after hardening; triple tempering at max. secondary hardening temperature is recommended; rapid cooling following the tempering improves the dimensional stability; maximum hardness achievable after tempering: 60-62 HRC

Annealing graph:


Technical tip:
  • secondary hardening, very good base material for nitriding or coating

To the mould making overview To the die making overview

Available in the web shop as:
Data sheet 1.2379

Abrir PDF

Folleto de materiales

Folleto de materiales

Póster de materiales

Póster de materiales

Iniciar sesión

¿Ya se ha registrado como cliente en el portal de Meusburger?

Si ya dispone de datos de acceso para el portal de Meusburger, inicie sesión aquí:

¿Ha olvidado la contraseña?

Ya hemos enviado la contraseña que acaba de crear. Debería recibirla en breve en su bandeja de entrada. ¡Qué tenga un día provechoso!

Introduzca una dirección de correo electrónico y
le enviaremos una contraseña nueva.

Selección de la tienda

Seleccione su país

Filiales