Kontakt

Vi står til rådighed mandag til fredag fra kl. 8:00 til kl. 17:00. Via dette link kan du finde din kontaktperson for dit område.

Din kontaktperson

+43 5574 6706-0

Din besked til os

Kurv {{ (warenkorbCtrl.warenkorb.bestellNummer ? (' [' + warenkorbCtrl.warenkorb.bestellNummer + '] ') : '' )}} | {{warenkorbCtrl.warenkorb.items.length}} Produkt   Skift indkøbskurv

Bemærkning

Billede Produkt Stk. Enkeltpris Samlet pris Samlet pris inkl. rabat
{{warenkorbItem.produktgruppe.produktname}}

{{warenkorbItem.bezeichnung | artikelBezFilter:warenkorbItem.attributwertEingaben}}

{{attributwertEingabe.attributBezeichnung}}

{{(warenkorbItem.aktionsBruttopreis || warenkorbItem.bruttopreis) | currency:warenkorbCtrl.warenkorb.waehrung:warenkorbCtrl.warenkorb.getFraction()}} Pris på forespørgsel {{(warenkorbItem.gesamtAktionsBruttopreis || warenkorbItem.gesamtBruttopreis) | currency:warenkorbCtrl.warenkorb.waehrung:warenkorbCtrl.warenkorb.getFraction()}} Pris på forespørgsel {{(warenkorbItem.gesamtAktionsBruttopreis || warenkorbItem.gesamtRabattBruttopreis) | currency:warenkorbCtrl.warenkorb.waehrung:warenkorbCtrl.warenkorb.getFraction()}} Pris på forespørgsel
{{hannexItem.Benennung}}

{{hannexItem.Bezeichnung}}

{{hannexItem.einzelpreis | currency:warenkorbCtrl.warenkorb.waehrung:warenkorbCtrl.warenkorb.getFraction()}} Pris på forespørgsel {{::((hannexItem.einzelpreis * hannexItem.Menge) | currency:warenkorbCtrl.warenkorb.waehrung:warenkorbCtrl.warenkorb.getFraction())}} Pris på forespørgsel {{hannexItem.gesamtpreis | currency:warenkorbCtrl.warenkorb.waehrung:warenkorbCtrl.warenkorb.getFraction()}} Pris på forespørgsel
Samlet beløb ekskl. moms:  {{warenkorbCtrl.warenkorb.calcGesamtpreis() | currency:warenkorbCtrl.warenkorb.waehrung:warenkorbCtrl.warenkorb.getFraction()}} Pris på forespørgsel

Log ind for at forsætte din bestilling.

Reduktion af spændinger

Vores udvalgte sortiment tilbyder det passende materiale til næsten alle anvendelser.

Franz Kohler
Head of Product Division

1.2162 Steel for case-hardening

Designation

DIN:21 MnCr 5
AFNOR:20 MC 5
UNI:-
AISI:5120 
 

Chemical composition:

C0.21
Si0.25
Mn1.25
Cr1.20
 

Strength:

≈ 660 N/mm²

Thermal conductivity at 100 °C:

38.5 W/m K


Character:

standard steel for case-hardening with good machinability; high surface hardness with tough core

Application:

machine parts and moulding plates with a high surface hardness;
synthetic resin press moulds for the processing of thermoplastics and thermosetting plastics.


Treatment by

possible:
Polishing, etching, EDM

Nitriding:
Usually, hardened parts are not nitrided → loss of hardness.

Hard chroming:
recommended, results in increased wear and corrosion resistance

 


Heat treatment:

Soft annealing:

670 to 710 °C for about 2 to 5 hours
slow controlled cooling, further cooling in air, max. 205 HB

Carburising:
900 to 950 °C. The choice of the carburising means and carburising temperature depends on the desired surface carbon content, the carburising graph and the required case depth.

 

Application:
870 to 930 °C in powder/salt bath, cooling in oil/warm bath at 160 to 250 °C

Intermediate stress-relieving heat treatment:
630 to 650 °C, about 2 to 4 hours with slow furnace cooling

Preheating:
350 °C depending on dimensions

Hardening:
curing temperature 810 to 840 °C in oil of ~ 60 °C warmth

Cooling:
down to about 100 °C in oil, then in air to about 50 °C

Tempering:
1 hour per 20 mm part thickness, at least 2 hours

Annealing graph:

 


Technical tip:
  • For mirror polishing we recommend the steel for through hardening 1.2767.

Available in the web shop as:
Data sheet 1.2162

Åbn pdf

Material grades brochure

Material grades brochure

Material grades poster

Material grades poster

Log ind

Er du allerede kunde?

Hvis du allerede har adgangsdata til Meusburgers portal, kan du logge ind her:

Glemt password?

Det nye password er på vej og burde snart ankomme i din indbakke. Vi ønsker god fornøjelse med starten.

Indtast venligst din e-mailadresse.
Vi sender dig et password.

Shop udvalg

Vælg dit land

Afdelinger